点击图片查看大图
ULTEM?
1000R resin
聚醚酰亚胺
产品说明:
ULTEM 1000R resin is an amorphous, opaque polyetherimide (PEI) plastic
offering a glass transition temperature (Tg) of 217°C. This inherently flame
retardant resin has UL94 V0, V2 and 5VA ratings and is RoHS compliant. ULTEM
1000R resin is an unreinforced general purpose grade offering high heat
resistance, high strength and modulus and broad chemical resistance up to high
temperatures with standard flow and standard mold
release.
| 塑料商城 | 塑料报价网 | PDF数据表 | UL 黄卡 |
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
||||
|
UL 黄卡 2
|
||||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
外观
|
|
|||
|
加工方法
|
|
|||
|
多点数据
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.27
|
g/cm?
|
ASTM D792 |
|
熔流率（熔体流动速率） (337°C/6.6
kg)
|
9.7
|
g/10 min
|
ASTM D1238 |
|
收缩率 - 流动 (3.20 mm)
|
0.50 到 0.70
|
%
|
内部方法 |
|
吸水率
|
ASTM D570 | ||
|
24
hr
|
0.25
|
%
|
|
|
平衡,
23°C
|
1.3
|
%
|
|
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度 (M 级)
|
109
|
|
ASTM D785 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量 3
|
3590
|
MPa
|
ASTM D638 |
|
抗张强度 4 (屈服)
|
110
|
MPa
|
ASTM D638 |
|
伸长率 4
|
ASTM D638 | ||
|
屈服
|
7.0
|
%
|
|
|
断裂
|
60
|
%
|
|
|
弯曲模量 5 (100 mm 跨距)
|
3520
|
MPa
|
ASTM D790 |
|
弯曲强度 5 (屈服, 100 mm
跨距)
|
165
|
MPa
|
ASTM D790 |
|
泊松比
|
0.36
|
|
ASTM D638 |
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17
转轮)
|
10.0
|
mg
|
ASTM D1044 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度 (23°C)
|
53
|
J/m
|
ASTM D256 |
|
无缺口悬臂梁冲击 (23°C)
|
1300
|
J/m
|
ASTM D4812 |
|
反向缺口冲击 (3.20 mm)
|
1600
|
J/m
|
ASTM D256 |
|
落锤冲击 (23°C)
|
36.6
|
J
|
ASTM D3029 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
ASTM D648 | ||
|
0.45 MPa,
未退火, 6.40 mm
|
210
|
°C
|
|
|
1.8 MPa,
未退火, 6.40 mm
|
201
|
°C
|
|
|
维卡软化温度
|
219
|
°C
|
ASTM D1525 6 |
|
线形热膨胀系数
|
ASTM E831 | ||
|
流动 : -20 到
150°C
|
5.6E-5
|
cm/cm/°C
|
|
|
横向 : -20 到
150°C
|
5.4E-5
|
cm/cm/°C
|
|
|
导热系数
|
0.22
|
W/m/K
|
ASTM C177 |
|
RTI Elec
|
170
|
°C
|
UL 746 |
|
RTI Imp
|
170
|
°C
|
UL 746 |
|
RTI
|
170
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
1.0E+17
|
ohms·cm
|
ASTM D257 |
|
介电强度
|
ASTM D149 | ||
|
1.60 mm, in
Air
|
33
|
kV/mm
|
|
|
1.60 mm, in
Oil
|
28
|
kV/mm
|
|
|
介电常数 (1 kHz)
|
3.15
|
|
ASTM D150 |
|
耗散因数
|
ASTM D150 | ||
|
1
kHz
|
1.3E-3
|
|
|
|
2.45
GHz
|
2.5E-3
|
|
|
|
耐电弧性 7
|
PLC 5
|
|
ASTM D495 |
|
相比耐漏电起痕指数(CTI)
|
PLC 4
|
|
UL 746 |
|
高电弧燃烧指数(HAI)
|
PLC 3
|
|
UL 746 |
|
高电压电弧起痕速率 (HVTR)
|
PLC 2
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 1
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
0.400
mm
|
V-2
|
|
|
|
0.750
mm
|
V-0
|
|
|
|
3.00
mm
|
5VA
|
|
|
|
极限氧指数
|
47
|
%
|
ASTM D2863 |
|
NBS Smoke Density - Flaming,
Ds, 4 min
|
0.700
|
|
ASTM E662 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
149
|
°C
|
|
|
干燥时间
|
4.0 到 6.0
|
hr
|
|
|
干燥时间，大
|
24
|
hr
|
|
|
建议的大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
332 到 399
|
°C
|
|
|
料筒中部温度
|
338 到 399
|
°C
|
|
|
料筒前部温度
|
343 到 399
|
°C
|
|
|
射嘴温度
|
343 到 399
|
°C
|
|
|
加工（熔体）温度
|
349 到 399
|
°C
|
|
|
模具温度
|
135 到 163
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
免责声明：（1）以上所展示的信息由企业自行提供，内容的真实性、准确性和合法性由发布企业负责，环球塑化网对此不承担任何保证责任。我们原则上建议您优先选择“塑企通”会员合作! （2）同时我们郑重提醒各位买/卖家，交易前请详细核实对方身份，切勿随意打款或发货，谨防上当受骗。如发现虚假信息，请向环球塑化网举报。